The amount of carbon present in steel determines its hardness and has serious implications for welding. Increased carbon content increases the tensile strength of steel but reduces its ductility and weldability. If the carbon content is above 0.25 percent, sudden cooling from the welding temperature may produce a brittle area next to the weld. The weld itself may be hard and brittle if an excess of carbon is picked up from the steel being welded. If other alloying elements are added to promote high tensile strength, good weld qualities can be retained. In general, an effort is made to use steels of low or medium carbon content.

Efectos de los elementos comunes en el acero - No metales. El carbono puro se encuentra en su estado nativo tanto en forma de diamante, un material muy duro, como de grafito, un material blando. El carbono es una parte del carbón, el petróleo, el asfalto y la piedra caliza. Comercialmente se puede obtener como negro de humo, carbón vegetal y coque.

La cantidad de carbono presente en el acero determina su dureza y tiene serias implicaciones para la soldadura. El aumento del contenido de carbono aumenta la resistencia a la tracción del acero, pero reduce su ductilidad y soldabilidad. Si el contenido de carbono está por encima del 0,25 por ciento, el enfriamiento repentino de la temperatura de soldadura puede producir un área quebradiza junto a la soldadura. La soldadura en sí puede ser dura y quebradiza si se extrae un exceso de carbono del acero que se está soldando. Si se agregan otros elementos de aleación para promover una alta resistencia a la tracción, se pueden conservar buenas cualidades en la soldadura. En general, se hace un esfuerzo por utilizar aceros de bajo o medio contenido en carbono.